Formation of intermetallic phases during solidification in Al-Mg-Mn 5xxx alloys with various Mg levels

Algendy Ahmed Y., Liu Kun et Chen X-Grant. (2020). Formation of intermetallic phases during solidification in Al-Mg-Mn 5xxx alloys with various Mg levels. MATEC Web of Conferences, 326, e02002.

[img]
Prévisualisation
PDF - Version publiée
Disponible sous licence Creative Commons Attribution.

826kB

URL officielle: http://dx.doi.org/doi:10.1051/matecconf/2020326020...

Résumé

In the present study, four Al-Mg-Mn 5xxx alloys with different Mg levels (2-5 wt.%) were investigated for better understanding the evolution of intermetallic phases formed during solidification. Optical and scanning electron microscopes, electron backscattered diffraction and differential scanning calorimetry analyses in combination with thermodynamic calculation were used to identify various intermetallic phases. Results showed that the most dominant intermetallic phases are Al6(Mn,Fe), α-Al(Fe,Mn)Si, Al3Fe, Alm(Mn,Fe) and Mg2Si in experimental Al-Mg-Mn alloys, which is greatly dependant on the Mg levels. It is found that Chinese script α-Al(Fe,Mn)Si is the dominant iron-rich intermetallic phase for the alloys containing 2-3 wt.% Mg, while blocky Al6(Mn,Fe) and needle-like Al3(Mn,Fe) become the major phases for the alloy containing 4 wt.% Mg. Further increasing Mg content to 5 wt. %, the dominant phase transfers to blocky Al6(Mn,Fe) intermetallic. Meanwhile, the morphology of primary Mg2Si is changed from well-branched to plate-like with increasing Mg contents. In addition, β-Al3Mg2 and τ-Al6CuMg4 eutectic phases have been observed in the alloys with 3-5 wt. % Mg. A comparison on various intermetallic phases from the Scheil simulation and the actual as-cast microstructure is provided.

Type de document:Article publié dans une revue avec comité d'évaluation
Volume:326
Pages:e02002
Version évaluée par les pairs:Oui
Date:5 Novembre 2020
Sujets:Sciences naturelles et génie > Génie
Sciences naturelles et génie > Génie > Génie des matériaux et génie métallurgique
Sciences naturelles et génie > Sciences appliquées
Département, module, service et unité de recherche:Départements et modules > Département des sciences appliquées > Module d'ingénierie
Mots-clés:Proceedings, Al-Mg 5xxx alloys, intermetallic phases, Mg2Si, solidification, alliages Al-Mg 5xxx, phases intermétalliques
Informations complémentaires:The 17th International Conference on Aluminium Alloys 2020 (ICAA17)
Déposé le:10 nov. 2021 22:25
Dernière modification:10 nov. 2021 22:25
Afficher les statistiques de telechargements

Éditer le document (administrateurs uniquement)

Creative Commons LicenseSauf indication contraire, les documents archivés dans Constellation sont rendus disponibles selon les termes de la licence Creative Commons "Paternité, pas d'utilisation commerciale, pas de modification" 2.5 Canada.

Bibliothèque Paul-Émile-Boulet, UQAC
555, boulevard de l'Université
Chicoutimi (Québec)  CANADA G7H 2B1
418 545-5011, poste 5630