Safaee Alireza, Sarkar Dilip K. et Farzaneh Masoud. (2008). Superhydrophobic properties of silver-coated films on copper surface by galvanic exchange reaction. Applied Surface Science, 254, (8), p. 2493-2498.
Prévisualisation |
PDF
442kB |
URL officielle: http://dx.doi.org/doi:10.1016/j.apsusc.2007.09.073
Résumé
Hydrophobic properties of thin nanostructured silver films produced by galvanic exchange reaction on a copper surface were studied after passivation with stearic acid. The morphology of the silver films was controlled by varying the concentration of silver nitrate in the solution. Water contact angle as high as 156° and contact angle hystérésis as low as 5° were achieved for samples obtained with initial silver ion concentration of 24.75 mM in the solution. However, a strong dependence of contact angle and contact angle hysteresis on the fractal-like morphology of the silver films was observed with the variation of silver ion concentration.
| Type de document: | Article publié dans une revue avec comité d'évaluation |
|---|---|
| Volume: | 254 |
| Numéro: | 8 |
| Pages: | p. 2493-2498 |
| Version évaluée par les pairs: | Oui |
| Date: | 15 Février 2008 |
| Sujets: | Sciences naturelles et génie > Génie > Génie des matériaux et génie métallurgique |
| Département, module, service et unité de recherche: | Départements et modules > Département des sciences appliquées > Module d'ingénierie |
| Mots-clés: | Superhydrophobicity, Microstructure, Electron microscopy, Galvanic exchange reaction, superhydrophobicité, microstructure, La microscopie électronique, réaction d'échange galvanique |
| Déposé le: | 22 sept. 2015 02:01 |
|---|---|
| Dernière modification: | 09 déc. 2016 13:34 |
Éditer le document (administrateurs uniquement)
Altmetric
Altmetric