A review of icephobic coating performances over the last decade

Laforte Caroline, Blackburn Caroline et Perron Jean. A review of icephobic coating performances over the last decade. Dans : SAE Technical Paper Series - SAE 2015 International Conference on Icing of Aircraft, Engines, and Structures , June 22-25, 2015, Prague, Czech Republic.

[thumbnail of A review of icephobic coating performances over the last decade.pdf] PDF
Administrateurs seulement



This paper depicts icephobic coating performances of 274 different coatings, including 11 grease-type coatings, which were tested over the past 10 years in various research projects at the Anti-Icing Materials International Laboratory (AMIL). Icephobic performance is evaluated using two comparative test methods. The first method, the ice Centrifuge Adhesion Test (CAT), measures the force required to separate the accreted ice from the coating (e.g. adhesive failure). The test involves simultaneously icing, under supercooled precipitation, the extremity of bare reference and freshly coated aluminum samples. The ice adhesion shear stress is calculated from the ice detachment rotation speed. The results are reported as Adhesion Reduction Factor (ARF), which is the ice adhesion stress on the bare aluminum reference samples divided by the ice adhesion stress on the coated samples. The second method is the Static ice Accumulation Test (SAT), by which the amount of ice accumulated on coated substrates set up at incidence angles of 45° and 80° is compared to uncoated Al surfaces inclined at the same angles. The results are reported in terms of Accumulation Reduction Factor (ACCRF), which is the ice mass on the bare aluminum samples divided by that accumulated on the coated samples. Overall, the performance of tested coatings over the years remains similar with a wide range of ARF values, 0.5 to 1000, corresponding to stresses between 0.8 MPa and 0.0005 MPa, respectively.

Type de document:Matériel de conférence (Non spécifié)
Sujets:Sciences naturelles et génie > Génie > Génie des matériaux et génie métallurgique
Département, module, service et unité de recherche:Départements et modules > Département des sciences appliquées > Module d'ingénierie
Mots-clés:aircraft deicing, coatings, colorants and finishes, icing and ice detection
Déposé le:27 oct. 2016 01:46
Dernière modification:09 déc. 2016 16:15
Afficher les statistiques de telechargements

Éditer le document (administrateurs uniquement)

Creative Commons LicenseSauf indication contraire, les documents archivés dans Constellation sont rendus disponibles selon les termes de la licence Creative Commons "Paternité, pas d'utilisation commerciale, pas de modification" 2.5 Canada.

Bibliothèque Paul-Émile-Boulet, UQAC
555, boulevard de l'Université
Chicoutimi (Québec)  CANADA G7H 2B1
418 545-5011, poste 5630