Liu Kun et Chen X-Grant. (2017). Evolution of microstructure and elevated-temperature properties with Mn addition in Al–Mn–Mg alloys. Journal of Materials Research, p. 1-9.
Prévisualisation |
PDF
- Version acceptée
1MB |
URL officielle: http://dx.doi.org/doi:10.1557/jmr.2017.239
Résumé
In the present work, various Mn amounts (up to 2 wt.%) have been added into Al-Mn-Mg 3004 alloy to study their effect on the evolution of microstructure and elevated-temperature properties. Results showed that the dominant intermetallics are interdendritical Al6(MnFe) until to 1.5 wt.% Mn. With further addition of Mn to 2 wt.%, the blocky primary Al6Mn/Al6(MnFe) and high volume of fine Al6(MnFe) intermetallics form in the matrix, leading to the rapid increase on the volume fraction of intermetallics. After the precipitation heat treatment (375°C/48h), the precipitation of dispersoids increased with increasing Mn contents and reached the peak condition in the alloy with 1.5 wt.% Mn, resulting in the highest yield strength and creep resistance at 300°C. However, the elevated-temperature properties became worse in the alloy with 2 wt.% Mn due to the lowest volume fraction of dispersoids and highest volume of dispersoid free zone.
| Type de document: | Article publié dans une revue avec comité d'évaluation |
|---|---|
| Pages: | p. 1-9 |
| Version évaluée par les pairs: | Oui |
| Date: | 22 Juin 2017 |
| Sujets: | Sciences naturelles et génie > Génie > Génie des matériaux et génie métallurgique |
| Département, module, service et unité de recherche: | Départements et modules > Département des sciences appliquées > Module d'ingénierie |
| Mots-clés: | Al-Mn-Mg 3004 alloy, Dispersoids, Mn contents, Elevated-temperature properties, Alliage Al-Mn-Mg 3004, Dispersoïdes, contenu de Mn, propriétés de température élevée |