Foroughi Mobarakeh Landan, Jafari Reza et Farzaneh Masoud. (2018). Robust icephobic, and anticorrosive plasma polymer coating. Cold Regions Science and Technology, 151, p. 89-93.
Le texte intégral n'est pas disponible pour ce document.
URL officielle: http://dx.doi.org/doi:10.1016/j.coldregions.2018.0...
Résumé
The durability of the superhydrophobic coatings is an important factor in the lifetime of a coating under extreme environmental conditions. In this study, a superhydrophobic surface was developed by using low pressure plasma polymerized HMDSO coatings on an anodized aluminum surface. The stability of coating was studied under accelerated aging conditions such as several icing/de-icing cycles, UV degradation, immersion in distilled water as well as corrosion. It was found that the developed surface can keep its superhydrophobicity (contact angle ~156°) as well as its icephobic properties even after up to 15 icing/de-icing cycles. It was also observed that the coating has a relatively good stability against UV degradation. In addition, the superhydrophobic surface can keep hydrophobic properties after 1000 h immersion in distilled water. Finally, the superhydrophobic plasma polymerized HMDSO coating also provides anti-corrosion protection for the aluminum substrate.
| Type de document: | Article publié dans une revue avec comité d'évaluation |
|---|---|
| Volume: | 151 |
| Pages: | p. 89-93 |
| Version évaluée par les pairs: | Oui |
| Date: | Juillet 2018 |
| Sujets: | Sciences naturelles et génie > Génie Sciences naturelles et génie > Génie > Génie des matériaux et génie métallurgique Sciences naturelles et génie > Sciences appliquées |
| Département, module, service et unité de recherche: | Départements et modules > Département des sciences appliquées > Module d'ingénierie Unités de recherche > Centre international de recherche sur le givrage atmosphérique et l’ingénierie des réseaux électriques (CENGIVRE) > Laboratoire des revêtements glaciophobes et ingénierie des surfaces (LaRGIS) |
| Mots-clés: | Plasma polymerization, hexamethyldisiloxane, stability, icephobicity, UV degradation, anti-corrosion, polymérisation plasma, stabilité, icephobie, dégradation UV |